Armand A Gregoli, Andrew M Olah: Low-temperature pipeline emulsion transportation enhancement. Canadian Occidental Petroleum, John Wade Carpenter, October 20, 1992: US05156652 (11 worldwide citation)

Stable oil-in-water emulsions for pipeline transmission are formed at a temperature of from about 100.degree. F. to about 200.degree. F. preferably using at least one ethoxylated alkylphenol compound and a freezing point depressant for water to enable pipeline transmission at temperatures below the ...


12
Carmen D Congelio, Andrew M Olah: Low volatile organic solvent based adhesive. The B F Goodrich Company, Helen A Odar, October 13, 1998: US05821289 (7 worldwide citation)

The present invention relates to a low VOC solvent based adhesive comprising a mixture of at least two organic solvents and a thermoplastic resin. Desirably the adhesive has a flash point of at least 100.degree. F. when measured in accordance with ASTM D3828-87. The solvent blend of the low VOC solv ...


13
Carmen D Congelio, Andrew M Olah: Low volatile organic solvent based adhesive. The B F Goodrich Company, Helen A Odar, October 6, 1998: US05817708 (7 worldwide citation)

The present invention relates to a low VOC solvent based adhesive comprising a mixture of at least two organic solvents and a thermoplastic resin. The low VOC solvent based adhesive of the instant invention volatilizes at substantially reduced rates as compared to conventional solvent based adhesive ...


14
Armand A Gregoli, Andrew M Olah, John A Hamshar, Daniel P Rimmer: Preparation of oil-in-aqueous phase emulsion and removing contaminants by burning. Canadian Occidental Petroleum, John Wade Carpenter, November 23, 1993: US05263848 (6 worldwide citation)

A process for preparing an oil-in-aqueous phase emulsion and removing contaminants from a contaminated hydrocarbon. The process comprises mixing a contaminated hydrocarbon with a reactant and an emulsifying composition. Contaminants are removed from the contaminated hydrocarbon either during the mix ...


15
Carmen D Congelio, Andrew M Olah: Low volatile organic solvent based adhesive. The B F Goodrich Company, Helen A Odar, October 5, 1999: US05962560 (5 worldwide citation)

The present invention relates to a low VOC solvent based adhesive comprising a mixture of at least two organic solvents and a thermoplastic resin. Desirably the adhesive has a flash point of at least 100.degree. F. when measured in accordance with ASTM D3828-87. The solvent blend of the low VOC solv ...


16
Carmen D Congelio, Andrew M Olah: Low volatile organic solvent based adhesive. B F Goodrich Company, Helen A Odar, January 12, 1999: US05859103 (2 worldwide citation)

The present invention relates to a low VOC solvent based adhesive comprising a mixture of at least two organic solvents and a thermoplastic resin having a flash point of at least 100.degree. F. when measured in accordance with ASTM D3828-87. The low VOC solvent based adhesive of the instant inventio ...


17
Michael P Perkovich, Andrew M Olah, Gary L Johnson, Stanley J Nerderman: System and method of assembly of CPVC fire sprinkler system employing mechanical couplings and supports. Lubrizol Advanced Materials, Joe A Powell, Samuel B Laferty, Thoburn T Dunlap, August 3, 2010: US07766092 (1 worldwide citation)

Fire sprinkler system comprising a network of CPVC pipe lengths in which at least some of the pipe lengths are interconnected with mechanical devices having resilient sealing members that are chemically compatible with the CPVC composition. Repairs and system modifications can be made without the us ...


18
Girish T Dalal, Arthur L Backman, Andrew M Olah, Theodore J Schmitz, Andrew L Auvil, Michael D Vaughn, James J Dedrick: Polyefinic pipe having a chlorinated polyolefinic hollow core. Noveon, Joe A Powell, January 9, 2007: US07160593

A multi-layered pipe of arbitrary length and cross-section is produced by co-extrusion of a lower polyolefin (C2–C4) outer body over the exterior surface of a tubular core of randomly, partially randomly, or blocky chlorinated lower polyolefin, the core having a wall thickness, measured in the radia ...


19
Arthur L Backman, Rocco A Mango, Robert S Newby, Andrew M Olah: CPVC pipe with 25% higher hydrostatic design basis than required under ASTM D2846. Lubrizol Advanced Materials, Samuel B Laferty, June 30, 2015: US09068072

CPVC pipe in diameters in the range from 15 mm (0.5 inch) to 15.24 cm (6 ins), to carry hot and cold aqueous streams under 690 KPa (100 psi) pressure and 82.2° C. (180° F.) in continuous service, is extruded from a compound in which the CPVC has a high Cl content in the range from 66.5%-70%, when mo ...


20
Garry L Fields, James D Burrington, Andrew M Olah: Polyacetylene and chlorinated polyacetylene and production processes thereof. Lubrizol Advanced Materials, Christopher P Demas, Teresan W Gilbert, March 8, 2016: US09279026

The present invention is directed to a heterogeneous gas phase polymerization process to produce true polyacetylene (PA; C2H2) in powder form, and the resultant PA product. The present invention is additionally directed to a chlorinated polyacetylene (CPA) compound comprised of primarily CHCl units ...