Jean Claude Decroix: Bitumen-polymer compositions for the preparation of road surface binders. Societe Chimique des Charbonnages, Finnegan Henderson Farabow Garrett & Dunner, March 17, 1987: US04650820 (34 worldwide citation)

The present invention provides a bitumen-polymer composition comprising 95 to 99% by weight of a bitumen and 1 to 5% by weight of a terpolymer having a melt index between 5 and 50 dg/min. The terpolymer comprises 88 to 98.7 mol % of units derived from ethylene; 1 to 10 mol % of units derived from at ...


2
Lionel Guerdoux: Multi-phase thermoplastic compositions and articles obtained therefrom. Societe Chimique des Charbonnages, Finnegan Henderson Farabow Garrett & Dunner, December 3, 1991: US05070145 (34 worldwide citation)

Compositions comprising from 50 to 95% by weight of at least one polyamide resin, and from 5 to 50% by weight % of a polymer composition comprising from 84 to 99.1 mole % of units derived from ethylene and from 0.9 to 16 mole % of units derived from an unsaturated anhydride of a dicarboxylic acid an ...


3
Jean Claude Decroix: Compositions for the manufacture of hot-melt adhesives. Societe Chimique des Charbonnages CDF CHIMIE, Finnegan Henderson Farabow Garrett & Dunner, September 13, 1983: US04404299 (33 worldwide citation)

A composition for the manufacture of hot-melt adhesives, in which the improvement comprises a terpolymer of ethylene having a melt index between 5 and 500 dg/minute and comprising from 1 to 10 mol % of units derived from an ester selected from alkyl acrylates and methacrylates, the alkyl group havin ...


4
Florent Raviola: Ethylene-propylene copolymers. Societe Chimique des Charbonnages, Finnegan Henderson Farabow Garrett & Dunner, January 3, 1984: US04424330 (32 worldwide citation)

A copolymer based on ethylene and propylene, having a density of between 0.933 and 0.946 g/cm.sup.3 and a melt index of between 2 and 10 dg/min, wherein the copolymer has from 3 to 27 alkyl groups per 1000 carbon atoms in the molecule and wherein its density .rho. and its proportion m of alkyl group ...


5
Jacques Hubert, Jean Marie Ory, Jean Bottin, Claude Humbert: Device for monitoring physical activity of persons. Societe Chimique des Charbonnages, Lerner David Littenberg & Samuel, August 29, 1978: US04110741 (27 worldwide citation)

An individual monitoring device is carried by a person whose movements are to be monitored. The monitoring device comprises a displacement detector arranged to supply a continuously variable signal dependent on the positional changes of the device, signal processing circuit receiving the signal and ...


6
Jean Pierre Machon, Genevieve Le Brasseur, Jean Claude Decroix, Marius Hert: Modified copolymers of ethylene and .alpha.-olefins and a process for their preparation. Societe Chimique des Charbonnages, Finnegan Henderson Farabow Garrett & Dunner, December 4, 1984: US04486579 (25 worldwide citation)

A modified copolymer of ethylene and of at least one .alpha.-olefin having from 3 to 12 carbon atoms, comprising from 0.5 to 10 mole percent of units derived from the .alpha.-olefin, wherein the measured limiting viscosity of the copolymer is between 1.5 and 10 times the limiting viscosity of the co ...


7
Jean Pierre Machon, Bernard Levresse, Pierre Gloriod: Deactivation of catalysts of the Ziegler type used for the preparation of polyethylene in high pressure, high temperature processes. Societe Chimique des Charbonnages, Lerner David Littenberg & Samuel, August 8, 1978: US04105609 (25 worldwide citation)

The present invention relates to a process for the continuous polymerisation and copolymerisation of ethylene under a pressure higher than 500 bars and at temperatures higher than about 160.degree. C in the presence of a catalyst containing a derivative of a transition metal and an organic derivativ ...


8
Armand Haas: Cold-stretchable, self-adhesive film composition. Societe Chimique des Charbonnages CdF Chimie, Finnegan Henderson Farabow Garrett & Dunner, November 25, 1986: US04624991 (23 worldwide citation)

A cold-stretchable, self-adhesive film composition comprising (a) from 88 to 97% by weight of an ethylene-.alpha.-olefin copolymer, the .alpha.-olefin having from 3 to 10 carbon atoms and the copolymer having a density of between 0.905 and 0.940 g/cm.sup.3 and a melt index of between 0.1 and 2 dg/mi ...


9
Marius Hert, Philippe Dufosse: Propylene and ethylene/.alpha.-olefin copolymer combinations applicable to the manufacture of mono-oriented yarns. Societe Chimique des Charbonnages, Finnegan Henderson Farabow Garrett & Dunner, January 7, 1986: US04563504 (21 worldwide citation)

A combination of at least one propylene polymer and at least one ethylene/.alpha.-olefin copolymer wherein the combination comprises: (a) 10 to 40 weight percent isotactic polypropylene; and (b) 60 to 90 weight percent ethylene/.alpha.-olefin copolymer, wherein said .alpha.-olefin has at least 4 car ...


10
Marius Hert: Compositions of ethylene polymers for the manufacture of films. Societe Chimique des Charbonnages, Finnegan Henderson Farabow Garrett & Dunner, November 18, 1986: US04623581 (20 worldwide citation)

A composition comprising from 2 to 25 weight percent of at least one free radical ethylene polymer with a specific gravity between 0.91 and 0.94, and from 75 to 98 weight percent of at least one copolymer of ethylene and at least one .alpha.-olefin containing at least 4 carbon atoms, with a specific ...